OKAYAMA GIKEN (Mining) Co., Ltd. has the most professional magnesia carbon brick manufacturing technology, we have formed the most standardized industry chain, we have the most professional manufacturing machinery and professional technology. Our magnesia-carbon bricks are sold all over the world and have been well received
OKAYAMA GIKEN (Mining) Co., LTD., has formed the most advanced manufacturing process, with the most professional manufacturing technology, magnesia carbon brick is often used in blast furnace, converter and electric arc furnace and other equipment, because of its excellent high temperature resistance and corrosion resistance, can effectively protect the furnace lining, extend the service life. Our magnesium-carbon bricks have more than 1500 high fire resistance, excellent corrosion resistance, good thermal conductivity, and the best mechanical strength.
OKAYAMA GIKEN (Mining) Co., Ltd. makes products with heart, faces every customer with a smile, and obtains praise from all customers with the best after-sales service, at the same time, we ensure that the products meet the highest industry standards. Choosing OKAYAMA GIKEN magnesium carbon brick can make your product get the best performance, at OKAYAMA GIKEN (Mining) Co., LTD., we always put the needs of customers in the first place and are committed to providing excellent service. Our professional team is not only experienced in the industry, but also able to tailor solutions to ensure the smooth running of every project. We respond quickly to customer inquiries, provide technical support and after-sales service to ensure that customers feel worry-free in the process of using our products. Choosing OKAYAMA GIKEN is not only to choose high-quality products, but also to choose a trustworthy partner, we will be happy to provide you with a full range of support and service.
| Applications | MFDCBrcks forconverter | MpO-C Bricks for electric f rnace | MgO-C Bricks for ladle | ||||||||
| Brand | ZLMT-16 | ZLMT-14 | ZLMT-12 | ZLMT-10 | DLMT-14 | DLMT-12 | DLMT-10 | DLMT-8 | GBMT-14 | GBMT-12 | GBMT-8 |
| MgO% ≥ | 76 | 77 | 80 | 80 | 76 | 76 | 78 | 80 | 76 | 78 | 82 |
| F/C% ≥ | 16 | 14 | 12 | 10 | 14 | 12 | 10 | B | 14 | 12 | 8 |
| B.D(g/cm³) | 2.93-3.02 | 2.95-3.03 | 2.96-3.03 | 2.98-3.05 | 2.93-3.02 | 2.95-3.03 | 2.96-3.03 | 2.98-3.05 | 2.93-3.02 | 2.95-3.03 | 2.96-3.03 |
| Apparent Porosity % ≤ | 3 | 4 | 4 | 5 | 4 | 5 | 6 | 6 | 4 | 5 | 6 |
| Cold Crushing Strength MPa ≥ | 40 | 40 | 35 | 35 | 40 | 35 | 30 | 30 | 40 | 35 | 30 |
| Hot Modulus of Rupture MPa ≥ | 10 | 10 | 6 | 5 | 10 | 8 | 6 | 5 | 12 | 10 | 6 |